Polyhydroxyalkanoate (PHBV) fibers obtained by a wet spinning method: Good in vitro cytocompatibility but absence of in vivo biocompatibility when used as a bone graft.

Polyhydroxyalkanoates (PHAs) are biomaterials widely investigated for tissue-engineering applications. In this regard, we describe a method to prepare fibers of poly(3-hydroxybutyrate-co-3-hydroxyvalerate) (PHBV) by a wet-spinning technique. Polymer fibers were used to test the cytocompatibility of the material in vitro. We have investigated their behavior in vitro in presence of the osteoblast-like (SaOs2) and macrophage (J774.2) cell lines. The PHBV fibers used were 100-200µm in diameter and offered a large surface for cell adhesion, similar to that they encounter when apposed onto a bone trabeculae. The fiber surface possessed a suitable roughness, a factor known to favor the adherence of cells, particularly osteoblasts. PHBV fibers were degraded in vitro by J774.2 cells as erosion pits were observable by transmission electron microscopy. The fibers were also colonisable by SaOs2 cells, which can spread and develop onto their surface. However, despite this good cytocompatibility observed in vitro, implantation in a bone defect drilled in rabbit femoral condyles showed that the material was only biotolerated without any sign of osteoconduction or degradation in vivo. We can conclude that PHBV is cytocompatible but is not suitable to be used as a bone graft as it does not favor osteoconduction and is not resorbed by bone marrow macrophages.

Properties of PHA bi-, ter-, and quarter-polymers containing 4-hydroxybutyrate monomer units.

The present study investigates physicochemical, mechanical, and biological properties of polyhydroxyalkanoate (PHA) copolymers containing 4-hydroxybutyrate (4HB) synthesized in Cupriavidus eutrophus B10646 culture. In poly(3-hydroxybutyrate/4-hydroxybutyrate) [P(3HB/4HB)] bipolymers, 4HB varied between 10.4 and 75.0 mol%; in poly(3-hydroxybutyrate/3-hydroxyvalerate/4-hydroxybutyrate) terpolymers, 4HB constituted 28.7-55.6 mol%; and in poly(3-hydroxybutyrate/3-hydroxyvalerate/4-hydroxybutyrate/3-hydroxyhexanoate) quaterpolymers, 4HB varied between 9.3 and 13.3 mol%. The degree of crystallinity of P(3HB/4HB) copolymers decreased consistently with an increase in 4HB content, reaching 38%. The incorporation of 3-hydroxyvalerate and 3-hydroxyhexanoate into copolymers enhanced that effect. The effect of 4HB monomer units on temperature properties of copolymers was exhibited as lowering of the melting temperature and crystallization temperature, which improved the processing-related properties of the copolymers. All copolymers containing 4HB showed enhanced elongation at break compared to poly(3-hydroxybutyrate). Polymer films prepared from PHAs with different chemical composition had similar microstructure and porosity and had no toxic effect on mouse fibroblast NIH 3 T3 cells, proving their high biocompatibility.

[The rat submandibular lymph node after introduction in mandibular bone defect ultipotent mesenchymal cells adsorbed on polyhydroxyalkanoate scaffold].

The reactions of rat regional lymph nodes, caused by implantation of the autologous multipotent mesenchymal stromal cells of a bone marrow origin (AMMSCBM) for acceleration of bone defect regeneration in bottom jaw experiment were studied by methods of fluorescent light microscopy. After introduction in an injury site of a bottom jaw bone of polyhydroxyalkanoate with adsorbed AMMSCBM with a transfected GFP gene the numerous large macrophages with a set of oval fluorescent inclusions in cytoplasm appear in lymph nodules of submandibular lymph nodes. The number of such macrophages increases within 2 weeks after operation, and further starts decreasing. Probably, entered via such way the AMMSCBM partially are phagocytized by macrophages. At destruction of the structures created from AMMSCBM, debris also are phagocytized by macrophages. In that and other case these macrophages appear in the germinative centers of lymph nodules in lymph nodes where initiation of immunity reactions against DNA and same GFP isn't excluded.

Reaction of the rat tissues to implantation of polyhydroxyalkanoate films and ultrafine fibers.

The reaction of various tissues of rats to implantation of polyhydroxyalkanoate films and ultrafine fibers was studied by optic microscopy. Implantation of polyhydroxyalkanoate films into the abdominal cavity caused a peritoneal reaction, leading after 1 month to the formation of fibrous adhesions between polyhydroxyalkanoate and intestinal loops. Under the skin and in the muscle tissue polyhydroxyalkanoate films were encapsulated in a thick fibrous capsule. Implantation of polyhydroxyalkanoate ultrathin fibers led to formation of foreign body granulomas in all tissues with perifocal inflammation and sclerosis of the adjacent tissues. The polymer was fragmented in these granulomas and phagocytosed by macrophages with the formation of giant foreign body cells. Hence, polyhydroxyalkanoate materials implanted in vivo caused chronic granulomatous inflammatory reaction and were very slowly destroyed by macrophages.